| Material | Hochmodul Polyäthylen |
Hochmodul
Polyester |
Hochmodul Polyamide |
Polyester | Polyamide | Polypro- pylen multifil |
Hempex | Nirodraht zum Vergleich Stainless |
| Handels- namen |
Dyneema SK75 |
Vectran | Kevlar, Twaron, Technora |
Diolen, Dacron, Trevira, etc. |
Nylon, Perlon, etc. |
Geolon | Spleitex | Zahlreiche Handels- namen |
| Festigkeit in g/den |
38 | 23 | 22-28 | 9 | 8-9 | 7-8 | 5-6 | |
| Festigkeit
in daN/mm2 |
360 | 230 | 250-400 | 110 | 90-95 | 70-75 | 50-55 | 180 |
| Bruch- dehnung |
3,80% | 3,30% | 3,40% | 10-17% | 18-24% | 14-17% | 14-17% | 1-2% |
| Art- gewicht g/cm3 |
0,97 | 1,4 | 1,44-1,45 | 1,40 | 1,14 | 0,91 | 0,91 | 7,4 |
| E-Modul in daN/mm2 |
10.500 | 10.000 | 13.000 - 15.000 |
1.000 - 1.500 |
25 - 350 |
50 - 500 |
400 | 14.000 |
| Schmelz-
punkt in °C |
140°C | 280°C | Carboni- sation at 500°C |
225°C | 215 - 260°C |
165
- 175°C |
165 - 175°C |
1000°C |
| UV- Beständig- keit |
sehr gut | begrenzt | begrenzt | sehr gut | gut | befriedigend | sehr gut | gut |
| Laugen- beständig- keit |
sehr gut | sehr gut | überwiegend gut |
bei
Raum- temperatur gut |
sehr
gut gegen schwache |
geg.
viele gut |
geg.
viele gut |
schlecht |
| Säuren- Beständig- keit |
sehr gut | sehr gut | überwiegend gut |
überwiegend gut |
überwiegend gut |
sehr gut | sehr gut | schlecht |
| Benzin-Öl Beständig- keit |
sehr gut | sehr gut | überwiegend gut |
sehr gut | gut | sehr gut | sehr gut | gut |
| Kriech- verhalten |
bei
hoher Last vorh. |
nicht messbar |
kaum messbar |
kaum messbar |
leichte Kriech- neigung |
in
hohen Last- bereichen |
in
hohen Last- bereichen |
messbar |
| Knoten- beständig- keit |
ca. 50% |
ca. 50% |
ca. 30% |
ca. 50% |
ca. 50% |
ca. 50% |
ca. 50% |
ca. 10% |
|
|
 |
 |